35#無縫管堆(dui)焊(han)處理時焊(han)劑選(xuan)擇的重(zhong)要性(xing)

35#無縫管獲得穩(wen)定(ding)電(dian)(dian)(dian)渣(zha)過程(cheng)(cheng)的(de)(de)另一個必要(yao)條件是(shi)焊(han)(han)(han)劑(ji)必須具有良好(hao)的(de)(de)導(dao)電(dian)(dian)(dian)性。一般(ban)電(dian)(dian)(dian)渣(zha)堆(dui)焊(han)(han)(han)焊(han)(han)(han)劑(ji)的(de)(de)電(dian)(dian)(dian)導(dao)率需(xu)達2～3Ω-1cm-1，為(wei)普通(tong)埋弧(hu)焊(han)(han)(han)焊(han)(han)(han)劑(ji)的(de)(de)4～5倍。國內外采用的(de)(de)電(dian)(dian)(dian)渣(zha)焊(han)(han)(han)劑(ji)多為(wei)燒結型。焊(han)(han)(han)劑(ji)電(dian)(dian)(dian)導(dao)率的(de)(de)大(da)(da)小(xiao)，取決于(yu)焊(han)(han)(han)劑(ji)組(zu)分(fen)中氯化物（NaF、CaF2、Na3AIF6等）的(de)(de)多少(shao)，當(dang)氯化物（質量分(fen)數(shu)）少(shao)于(yu)40%，堆(dui)焊(han)(han)(han)過程(cheng)(cheng)為(wei)電(dian)(dian)(dian)弧(hu)過程(cheng)(cheng)，在40%～50%范圍大(da)(da)致(zhi)是(shi)電(dian)(dian)(dian)弧(hu)、電(dian)(dian)(dian)渣(zha)聯合過程(cheng)(cheng)；當(dang)氯化物大(da)(da)于(yu)50%后，可(ke)形成全(quan)電(dian)(dian)(dian)渣(zha)過程(cheng)(cheng)。CaF2既是(shi)良好(hao)的(de)(de)導(dao)電(dian)(dian)(dian)材料(liao)又是(shi)主(zhu)要(yao)的(de)(de)造渣(zha)劑(ji)，因此CaF2通(tong)常是(shi)電(dian)(dian)(dian)渣(zha)堆(dui)焊(han)(han)(han)焊(han)(han)(han)劑(ji)的(de)(de)主(zhu)要(yao)成分(fen)。

除了導電性外，焊劑還需有良好的35#無縫管堆焊工藝性（脫渣、成形、潤濕性）及良好的冶金特性（合金元素燒損小，不利元素增量少），適宜的粒度（一般比埋弧焊焊劑粒度細）。滿足上述要求，已用于生產的焊劑種類很多，如有國外的FJ-1（日本）、EST122（德國）、Sandvik37S（美國）；國產的SJ15、SHD202等等。
 

文章來源：//jp-chudian.com/